Poliuretano elastomer formed by the polymerization reaction of diisocyanate and active hydrogen compound, the rigid segment containing urea group composed of diisocyanate and diamine chain extender, the glass transition temperature is much higher than room temperature, and it is glassy at room temperature. Subcrystals or microcrystals form the plastic phase; flexible segments of polyether or polyester are gathered together to form the matrix or matrix of the poliuretano rubber. Because its glass transition temperature is lower than room temperature, it is called the rubber phase. The microphase separation of the poliuretano elastomer makes the poliuretano elastomer have the advantages of good wear resistance, wide range of hardness, high strength and high elongation, large load supporting capacity, good shock absorption effect and excellent oil resistance. Choosing a suitable molding and processing method can maximize the performance of poliuretano elastomers and prepare various poliuretano elastomers with excellent properties, which are widely used as plastics, rubber, fibers, adhesives and coatings, and even as functional polymer materials. Such as medical poliuretanomateriais.
1.1 Princípios gerais para a seleção de métodos de processamento de conformação
(1) O processamento de moldagem é geralmente para derreter ou deformar um composto de polímero em um estado sólido (pó ou granular), pasta ou estado de solução e formar a forma desejada através de um molde e manter a forma que foi obtida e, finalmente, obter o produto. processo de elaboração.
(2) Fluxo de processamento de moldagem comum: - O método de formar a mistura de composto de polímero uma e duas vezes para produzir produtos; “O método de formação do composto de polímero para produzir produtos de uma só vez; • O método de produção de produtos a partir da mistura de monômeros em uma etapa • Método de produção de uma etapa da mistura de oligômeros.
(3) Desempenho de processamento e seus fatores de influência: - Capacidade de compressão, na extrusora, no tambor da máquina de injeção, nos rolos da calandra e no molde, quando o material é deformado por extrusão, a forma do material é obtida e capacidade mantida. Seus fatores restritivos: viscosidade do fundido, estrutura do equipamento de processamento, reologia do fundido e taxa de fluxo do fundido. “Moldabilidade, no processo de moldagem sob a ação da máquina de injeção, extrusora e máquina de compressão, o material é deformado sob a ação da temperatura e pressão e a capacidade de ser moldado no molde. Seus fatores restritivos: reologia, propriedades térmicas e outras propriedades físicas e mecânicas e reatividade química de compostos poliméricos. â ‘¢ Extensibilidade, na calandragem ou alongamento, o material é deformado por calandragem ou alongamento em uma ou duas direções. Seus fatores restritivos: a plasticidade do material e o efeito de endurecimento por deformação. â ‘£ Spinnability, o bocal durante a moldagem por extrusão, a capacidade do material de formar fibras sólidas contínuas por meio da moldagem. Seus fatores restritivos: reologia, viscosidade e resistência do fundido, estabilidade térmica e estabilidade química.
1.2 Princípios gerais para a seleção de métodos de moldagem e processamento parapoliuretanoelastômeros
Poliuretano elastomer molding processing system is divided into liquid system and solid system. On the basis of the rapid polymerization reaction of diisocyanate and active hydrogen compound, the molding processing method is conducive to the microphase separation of the poliuretano elastomer. , Liquid system, poliuretano casting glue can be processed by casting (manual casting, centrifugal casting and vacuum casting), reaction injection molding, spraying, knife coating, roller coating, laminating, laminating, bonding, vulcanizing, pasting and rubbing ; Solid system, poliuretano compound rubber can be vulcanized and laminated with mold, poliuretano thermoplastic can be used with thermoplastic, hot injection, calendering, blow molding, spinning and lamination.
1.3 O princípio de combinação de tipos básicos e métodos de processamento de moldagem
Poliuretanoo elastômero é um polímero de alto nível entre o plástico e a borracha em termos de módulo. Inclui principalmentepoliuretano compound rubber, poliuretano cast rubber, poliuretano water emulsion and poliuretano thermoplastic. Poliuretano leather, poliuretano adhesives, poliuretano coatings, poliuretano compounds, poliuretano casting glues, poliuretano fibers, poliuretano water emulsions and poliuretano thermoplastics are all derived from the above four types of glue. The molding and processing methods of poliuretano compound rubber, poliuretano water emulsion and poliuretano thermoplastic generally belong to the molding processing methods of rubber, coatings and plastics.
1.4 The use of poliuretano elastomers and the matching principle of production continuity and molding processing methods
Poliuretano elastomer molding and processing methods are matched with the use of poliuretano elastomers, taking into account the continuity of production. For example, poliuretano leather molding methods usually use poliuretano casting adhesive or foaming layer, poliuretano water emulsion and poliuretano thermoplastic as the surface layer; also available Poliuretano thermoplastic and poliuretano water emulsion are used as leather separately, which are based on the basic rubber molding processing method, supplemented by foam molding processing, usually calender molding processing method is selected. Poliuretano paving materials are made of poliuretano casting glue, mainly due to the large product shape and low precision requirements. Medical poliuretano materials have good chemical stability, tissue compatibility, and resistance to biological aging, so the molding process uses dip coating, pouring and coating methods.